Abstract

• The purpose of this work was to synthesize Pb1-xCaxTiO3 (x = 0, 0.1, 0.2, 0.3 wt%) in the form of powder phase by solid state mixed oxide technique and to study the structural properties of this laboratory-made PbCaTiO3 specimen by a systematic analysis of XRD and SEM for the potential applications in the ferroelectric devices. From XRD results, PbCaTiO3 powders were significantly formed with tetragonal symmetry. According to SEM results, these PbCaTiO3 powders were composed of regular and sphere grains with sizes ranging from (278.5 nm-433.75 nm) for various x contents. The PbCaTiO3 powders were quite suitable for cost effective and uncomplicated trends of ferroelectric materials such as random access memory (RAM).